ER5183


Used for the welding ocean,cold storage industry and structural application with an extremely high requirement to the high-strength,high impact fracture toughness and corrosion resistance,as well as the low-temperature storage tanks,railway industry,chemistry,food,ships,aerospace etc.Such as 5083 and 5654 base materials.

info@czyunhe.com

Product Introduction



Application: Used for the welding ocean,cold storage industry and structural application with an extremely high requirement to the high-strength,high impact fracture toughness and corrosion resistance,as well as the low-temperature storage tanks,railway industry,chemistry,food,ships,aerospace etc.Such as 5083 and 5654 base materials.

Characteristics: YH15183 is used for welding the base materials with a high magnesium content and high tensile strength or seawater corrosion resistance.This welding wire has excellent welding process properties with a beautiful formation of weld,stable electric arc and less splash.Used for the welding of 6xxx,6xxx and 5xxx.It is usually not recommended for the welding with a requirement of high temperature resistance due to its joint is sensitive to stress corrosion crack.

Chemical Composition Of Welding Wire:(Mass Fraction)

Item

Si

Fe

Cu

Mn

Mg

Cr

Zn

Ti

Al

Be

Guarantee Value

≤0.40

≤0.40

≤0.10

0.05 -1.0

4.3 -5.2

0.05 -0.25

≤0.25

0.15

Remain

≤0.0003

Typical Value

0.08

0.12

0.006

0.65

4.75

0.130

0.005

0.080

Remain

0.0001

Mechanical Properties Of Deposited Metal:(CO₂)

Item

Tensile Strength Rm/MPa

Yield Strength ReL/Rp0.2MPa

Elongation A%

Typical Value

280

150

18

Welding Method:MIG Gas:99.99%Ar

Physical Properties:

Melting Temperature(℃)

Density(g/cm³)

579-638

2.65

Welding Reference Current:(Current Polarity:MIG DC+TIG AC)

MIG

Wire Size(mm)

1.2

1.6

2.0

Welding Current(A)

180-300

200-400

240-450

Welding Voltage(V)

18-28

20-20

22-34

TIG

Wire Size(mm)

1.6-2.5

2.5-4.0

4.0-5.0

Welding Current(A)

150-250

200-320

220-400

Note On Usage:

1.It is required to remove the oxidation film and oil contaminant from the welding edge workpiece and surface of welding wire.

2.Itis able to support the molten metal with a plate during weldng to ensure the formation of weld.

 

Used for high eficiency welding in all positions with excellent welding performance such as warming electric arc,little spatters,beautiful seam forming and easily moved slag.Suitable for welding of 590 MPA high strength steel,steel structure,bridge,steel pipes,railway vehicle,and construction equipment etc.

Keywords:

ER5183

Product Message



*Attention: Please ensure accurate information filling and maintain smooth communication. We will contact you as soon as possible