ER307Si
Category:
Product Introduction
Application : Used for the welding of non-magnetic,high manganese steel and hardening corrosion-resisting steel,mostly used for the special nonmagnetic circumstances e.g.nuclear submarine,armor plate etc.,as wellas the welding of dissimilar steels with difficult welding and easy cracking.
Characteristics: This welding wire is 21%Cr-9%Ni-6%Mn austenitic stainless steel welding wire with a high Mn content,low cracking susceptibility,stable welding art and beautiful formation of weld.It has a good fluidity due to adding Si moten iron.Available for the all-positioning welding.
Chemical Composition Of Welding Wire:(Mass Fraction)
|
Item |
C |
Mn |
Si |
Cr |
Ni |
Mo |
P |
S |
Cu |
|
Guarantee Value |
0.04-0.14 |
6.50-8.00 |
0.65-1.00 |
18.50-22.00 |
8.00-10.70 |
≤0.75 |
≤0.030 |
≤0.030 |
≤0.75 |
|
Typical Value |
0.071 |
6.75 |
0.72 |
18.85 |
8.9 |
0.16 |
0.014 |
0.012 |
0.18 |
Mechanical Property of Deposited Metal
|
Item |
Tensile Strength Rm/MPa |
Elongation A% |
|
Typical Value |
605 |
38 |
Note On Usage:
1.The appropriate flow rate for MIG weding shielding gas is 18-25L/min;The protective ga1.MIG welding shield gasflow should be between 18-25L/min;The shield gas should apply Ar +2%O₂;If the wind speed is greater than 0.5m/s,it is required to take the wind-proof measures.
2.TIG welding shield gas flow requirement:If the welding current is between(15-200)A, the gas flow should be(5-14)L/min;If the welding current is between(200-320)A,the gas flow should be(14-24)L/min.The shield gas should apply pure Ar,and please take the wind-proof measures is the wind speed is greater than 1.0m/s;It is required to remove the impurities e.g. rust,oil contaminant,water etc.on welding workpiece prior to MIG/TIG welding;The above- mentioned welding parameters should be for reference only,users should develop the welding standards appropriate for the production according to their own specific conditions.
Used for high eficiency welding in all positions with excellent welding performance such as warming electric arc,little spatters,beautiful seam forming and easily moved slag.Suitable for welding of 590 MPA high strength steel,steel structure,bridge,steel pipes,railway vehicle,and construction equipment etc.
Keywords:
ER307Si
Product Message
*Attention: Please ensure accurate information filling and maintain smooth communication. We will contact you as soon as possible
YUNHE WELDING MATERIAL
Share to
Information Subscription
Welcome to leave your message of interest, we will contact you soon
Yaoguan Town, Wujin District, Changzhou, Jiangsu, China
Copyright©2025 Changzhou City Yunhe Welding Material Co.,Ltd.