ER308LSi
Category:
Product Introduction
Application: Used for the welding of materials with atmosphere corrosion resistance e.g. railway locomotives,truck body etc.Such as the welding of materials e.g.022Cr19Ni10(S304L) stainless steel,TCS used for transportation trucks etc.
Characteristics: This welding wire is 21%Cr-10%Ni ultra-low carbon austenitic stainless steel welding wire with a stable welding arc.Its molten iron has a good fluidity due to adding Si with a more beautiful formation of weld,available for the all-positioning welding
Chemical Composition Of Welding Wire:(Mass Fraction)
|
Item |
C |
Mn |
Si |
Cr |
Ni |
Mo |
P |
S |
Cu |
|
Guarantee Value |
≤0.030 |
1.00 -2.50 |
0.65 -1.00 |
19.50 -22.00 |
9.00 -11.00 |
≤0.75 |
≤0.030 |
≤0.030 |
≤0.75 |
|
Typical Value |
0.021 |
2.08 |
0.72 |
19.85 |
10.52 |
0.032 |
0.018 |
0.011 |
0.015 |
Mechanical Property of Deposited Metal
|
Item |
Tensile Strength Rm/MPa |
Elongation A% |
|
Guarantee Value |
≥510 |
≥25 |
|
Typical Value |
595 |
40 |
Note On Usage:
1.MIG welding shield gas flow should be between 18-25L/min;The shield gas should apply Ar+2%O₂;If the wind speed is greater than 0.5m/s,it is required to take the wind-proof measures.
2.TIG welding shield gas flow requirement:If the welding current is between(15-200)A, the gas flow should be(5-14)L/min;If the welding current is between(200-320)A,the gas flow should be(14-24)L/min.The shield gas should apply pure Ar,and please take the wind-proof measures is the wind speed is greater than 1.0m/s;It is required to remove the impurities e.g. rust,oil contaminant,water etc.on welding workpiece prior to MIG/TIG welding;The above- mentioned welding parameters should be for reference only,users should develop the welding standards appropriate for the production according to their own specific conditions.
Used for high eficiency welding in all positions with excellent welding performance such as warming electric arc,little spatters,beautiful seam forming and easily moved slag.Suitable for welding of 590 MPA high strength steel,steel structure,bridge,steel pipes,railway vehicle,and construction equipment etc.
Keywords:
ER308LSi
Product Message
*Attention: Please ensure accurate information filling and maintain smooth communication. We will contact you as soon as possible
YUNHE WELDING MATERIAL
Share to
Information Subscription
Welcome to leave your message of interest, we will contact you soon
Yaoguan Town, Wujin District, Changzhou, Jiangsu, China
Copyright©2025 Changzhou City Yunhe Welding Material Co.,Ltd.