EM12K(S2Si)


Used for the union melt welding of carbon steels,low alloy steels with corresponding strength grade e.g.ships,petrochemical engineering,boilers etc.

info@czyunhe.com

Product Introduction



Application: Used for the union melt welding of carbon steels,low alloy steels with corresponding strength grade e.g.ships,petrochemical engineering,boilers etc.

Characteristics: YHEM12K is used with sintered flux SJ101 with a stable arc combustion,beautiful formation of weld and easy deslagging.The weld has a good low- temperature impact toughness.

Chemical Compostion Of Welding Wires:(Mass Fraction)

Item

C

Mn

si

S

P

Cu

Guarantee Value

0.05-0.15

0.80-1.25

0.10-0.35

≤0.030

≤0.030

≤0.35

Typical Value

0.07

1.06

0.21

0.004

0.008

0.115

Mechanical Property of Deposited Metal

Item

Tensile Strength Rm/MPa

Yield Strength ReL/Rp0.2 MPa

Elongation
A%

Compound V-Type Notch
Impact Absorption KV₂ (J)
-20℃

Flux

Guarantee Value

430-560

≥330

≥22

≥27

SJ101

Typical Value

492

390

27

90

Note On Usage:

1.The welding flux should be used at 250-400℃ for baking 1 to 2 hours.Welding wire should be dry without oil or rust.

2.Please remote the impurities e.g.rust,oil contaminant and water etc.on welding workpiece prior to welding.

 

Used for high eficiency welding in all positions with excellent welding performance such as warming electric arc,little spatters,beautiful seam forming and easily moved slag.Suitable for welding of 590 MPA high strength steel,steel structure,bridge,steel pipes,railway vehicle,and construction equipment etc.

Keywords:

EM12K(S2Si)

Product Message



*Attention: Please ensure accurate information filling and maintain smooth communication. We will contact you as soon as possible