YHE71T-1Ni


Applicable to the welding for ships,bridges,steel structure and construction.

info@czyunhe.com

Product Introduction



Application: Applicable to the welding of 490MPa high-strength steel structure,mostly the welding of steel structure for ships,mechanical manufacturing,containers,petrochemical engineering,bridges etc.

Characteristics: YHE71T-1Ni is rutile slag system CO₂gas shield flux-core welding wire with excellent welding process properties,stable electric arc,less splash,easy deslagging and beautiful formation of weldRely on the good all-position weding process property,its weld metal has a good plasticity and low-temperature toughness.

Welding Wire Chemical Composition:(Mass Fraction)

Item

C

Mn

Si

P

S

Ni

Mo

Cr

Guarantee Value

≤0.18

≤1.75

≤0.90

≤0.030

≤0.030

≤0.50

≤0.30

≤0.20

Typical Value

0.050

1.37

0.35

0.015

0.006

0.34

0.08

0.012

Mechanical Properties Of Deposited Metal:

Item

Tensile Strength Rm/MPa

Yield Strength ReL/Rp0.2 MPa

Elongation A%

Impact Value KV(J)-40℃

X-Ray

Guarantee Value

≥480

≥400

≥22

≥27

Typical Value

550

470

26

110

Recommended Welding Parameter:(DC+)

Wire Size(mm)

1.2

Curremt(A)

100-280

Voltage(V)

20-32

Note On Usage:

1.Apply CO₂gas shield,and CO₂gas purity is above 99.95%.

2.The CO₂shield gas flow during welding should be controlled between 20~25L/min.

3.The extension elongation of welding wire should be controlled between 15~25mm.

4.The preheat and interpass temperature should be 150℃±15℃ .

 

Used for high eficiency welding in all positions with excellent welding performance such as warming electric arc,little spatters,beautiful seam forming and easily moved slag.Suitable for welding of 590 MPA high strength steel,steel structure,bridge,steel pipes,railway vehicle,and construction equipment etc.