  • Product name: STAINLESS STEEL WIRE
  • Product code: 017
  • Date: 2016-09-03
  • Views : 84

We just use very high-quality materials and lean mannfacturing of stainless steel welding wire.End products meet end users,critical demand and are widely used in the industries of shipment,petrochemical,refinery and automotive.Specifications and package can be adjusted in accordance with customers,special requirement.

 

Brand AWS GB/T 1785-99(YB/T 5092-96)

JIS

Z3321-99

Welding wire chemical composition(%)
C Mn Si Cr MO Ni Other
YH-307 ER307 - - 0.070 3.95 0.47 20.40 - 9.65 -
YH-308 ER308 H0Cr21Ni10 Y308 0.040 1.82 0.34 20.13 - 9.50 -
YH-308L ER308L H00Cr21Ni10 Y308L 0.024 1.65 0.42 20.10 - 10.33 -
YH-309 ER309 H1Cr24Ni13 Y309 0.083 1.65 0.42 23.83 - 13.13 -
YH-309L ER309L H00Cr24Ni13 Y309L 0.023 1.98 0.39 23.83 - 12.90 -
YH-309LSi ER309LSi - - 0.022 1.55 0.87 24.10 - 13.00 -
YH-310 ER310 H1Cr26Ni21 Y310 0.086 2.01 0.40 27.40 - 21.80 -
YH-316 ER316 H0Cr19Ni12Mo2 Y316 0.050 1.78 0.6 19.61 2.30 12.50 -




Brand Mechanical properties of deposited metal Application
Tensile strength
(MPa)
Elongation
(%)
YH-307 612 43 Welding seam strength can be controlled.Primarily used for welding of austenitic manganese steel forgings and casting,and austcnitic carbon steel forgings and castings with outstanding cracj resistance.Applicable to the protection of gas;Ar.
YH-308 607 41 Apply to the high binding conditions or fully austenitic metal cladding where a stable arc,good welding properties of Ar+(0.5%-2%)O2gas shielded welding.
YH-308L 578 42 Primarily used for welding of 18Cr-8No steel.The welding will have more outstanding resistance than MIG308,if they are used for welding of SUS304L.
YH-309 607 40 Used for dissimilar metel welding,such as the welding of mild steel and Cr-Mo steel,welding SUS309S,SCS17,Such as heat,corrosive,and arc stability,excellent welding performance,Ar=(0.5%-2%)o2gas shielded welding,similar to composite layers of ateel for carbon steel shell-side and in the lining of welded stainless steel sheet.
YH-309L 558 43
YH-309LSi 557 32 Primarily used for welding of high silicon,low carbon,22Cr-12Ni steels.
YH-310 607 41 25Cr-20Ni steel,such as more suitable for a varirty of MIG309L metal welding and self-rigid high-alloy steel and high carbon steel connections steel welding dissimilar components used and the furnace temperature below 950℃ gas system components.
YH-316 578 38 10Cr-12Ni-2.5Mo(SUS316)used for welding steel,as well as operating temperature of 600~750℃ chemical,oil refining tube heat exchangers,furnce tubes Peter.

Brand AWS A5.9-93 GB/T 1785-99(YB/T 5092-96)

JIS

Z3321-99

Welding wire chemical composition(%)
C Mn Si Cr MO Ni Other
YH-316L ER316L H00Cr19Ni12Mo2 Y316L 0.025 1.91 0.42 19.10 2.57 12.58 -
YH-316LSi ER316LSi - - 0.021 1.95 0.77 19.2 2.58 13.45 -
YH-317 ER317 H0Cr19Ni14Mo3 Y317 0.048 1.86 0.45 19.41 3.51 14.23 -
YH-317L ER317L H00Cr19Ni14Mo3 Y317L 0.023 1.76 0.40 19.60 3.63 13.68 -
YH-321 ER321 H0Cr20Ni10Ti Y321 0.062 1.74 0.49 19.50 - 9.57 Ti:0.82
YH-347 ER347 H0Cr20Ni10Nb Y347 0.030 1.61 0.41 20.37 - 9.90 Ti:0.80
YH-410 ER410 H1Cr13 Y410 0.100 0.43 0.45 11.81 - 0.17 -
YH-430 ER430 H1Cr17 Y430 0.083 0.46 0.39 16.37 - 0.20 -
YH-502 ER502 H1Cr5Mo - 0.084 0.53 0.42 5.60 0.59 0.37 -




Brand Mechanical properties of deposited metal Application
Tensile strength
(MPa)
Elongation
(%)
YH-316L 558 40 10Cr-12Ni-2.5Mo(SUS316)used for welding steel,as well as operating temperature of 600~750℃ chemical,oil refining tube heat exchangers,furnce tubes Peter.
YH-316LSi 562 31 Primarily used for welding of hight silicon,low carbon,18Cr-12Ni-2.5Mo steels.
YH-317 598 42 Primarily used for welding of 18Cr-12Ni-3.5Mo steels.With outstanding resistance to sulphuruic acid,sulphurous acid and other organic acids,exceptional resistance to pitting corrosion and heat,the welding wires are espexially suitable for welding of chemical containers.
YH-317L 568 42 Primarily used for welding of low carbon 18 Cr-12Ni-3.5Mo steels,low carbon and high molybdenum steels.The welding wires can avoid intergranular corrosion.Finished welded parts can free heat treatment.The welding wires have high-temperature strength and outstanding resistance to sulphuric acid,sulphurous acid and other organic acids.
YH-321 562 39 Primarily used for welding of 20 Cr-10Ni-Ti steels,thanks to Ti added,the welding wires have greatly increased resistance to resisting steels.
YH-347 627 41 Primarily used for welding of 18 Cr-10Ni-Ti steels,thanks to Nb added,the welding wires have greatly increased resistance to intereanular corrosion and outstanding high-tem perature strength.Especially suitable for welding of high temperature resisting steels.
YH-410 510 25 Primarily used for welding of 13 Cr steels.Deposited metals are 13Cr with large harden ability.Thanks to outstanding resistance to oxidation and corrosion at high temperature.The welding wires are especially suitable for welding of ALS1410 or 420..
YH-430 585 36 Primarily used for welding of 17Cr steels,especially suitable for welding of nitric acid containers.
YH-502 608 34 Primarily used for welding of 1Cr5Mo steels,suitable for welding among pipes.Pre-heating and post-heating for welding are required.